ASTM A53 B ERW Paipa UameaFa'atatauga
1 Fa'ata'ita'iga: pito sili ona maualuga o le paipa i lalo o le tele o su'esu'ega o le eleele pe a olo, fa'avela, fe'avea'i vai vevela ma isi.
2 Masini, seti faʻapipiʻi, masini gaosi ma isi mea faʻaoga.
3 Vasega eletise: tufatufa kesi, alavai vai eletise.
4 Anti-static tubes fale malosi matagi.
ASTM A53 B ERW Pipe Uamea e aofia ai ituaiga ma togi:
Ituaiga E—E-tetee-eletise-uelo, Vasega A ma le B
Kemisi o ASTM A53 B ERW Paipa Uamea
| Ituaiga | kaponi maualuga. % | Manganese maualuga. % | Phosphorous maualuga. % | Sulfur maualuga. % | Kopa maualuga. % | Nikeli maualuga. % | Chromium maualuga. % | Molybdenum maualuga. % | ||||||||
| Vasega A | Vasega B | Vasega A | Vasega B | Vasega A | Vasega B | Vasega A | Vasega B | Vasega A | Vasega B | Vasega A | Vasega B | Vasega A | Vasega B | Vasega A | Vasega B | |
| Ituaiga E (uila fa'aeletise) | 0.25 | 0.30 | 0.95 | 1.2 | 0.05 | 0.05 | 0.045 | 0.045 | 0.40 | 0.40 | 0.40 | 0.40 | 0.15 | 0.15 | 0.08 | 0.08 |
Tensile o ASTM A53 B ERW Paipa Uamea:
| Tensile | Eletise-tetee-uelo
| |
| Vasega A | Vasega B | |
| Malosi Tetele min. psi | 48,000 | 45,000 |
| Malosi e maua min. psi | 30,000 | 25,000 |
Fa'amatalaga ole ASTM A53 B ERW Pipe Uamea
| Malosi o Pa | I fafo Diamita | ||||||||||||||||||
| Inisi | mm | inisi | mm | inisi | mm | inisi | mm | inisi | mm | inisi | mm | inisi | mm | inisi | mm | inisi | mm | inisi | mm |
| 8 5/8 | 219.1 | 10 3/4 | 273.1 | 12 3/4 | 325.0 | 14 | 355.6 | 16 | 406.4 | 18 | 457.7 | 20 | 508.0 | 24 | 610 | 24 4/5 | 630.0 | ||
| 0.157 | 4.0 | l | l | ||||||||||||||||
| 0.197 | 5.0 | l | l | l | l | l | l | l | l | ||||||||||
| 0.236 | 6.0 | l | l | l | l | l | l | l | l | l | l | l | l | ||||||
| 0.276 | 7.0 | l | l | l | l | l | l | l | l | l | l | l | l | l | |||||
| 0.315 | 8.0 | l | l | l | l | l | l | l | l | l | l | l | l | l | l | l | l | ||
| 0.354 | 9.0 | l | l | l | l | l | l | l | l | l | l | l | l | l | l | l | l | ||
| 0.394 | 10.0 | l | l | l | l | l | l | l | l | l | l | l | l | l | l | l | l | l | l |
| 0.433 | 11.0 | l | l | l | l | l | l | l | l | l | l | l | l | l | l | l | l | l | l |
| 0.492 | 12.5 | l | l | l | l | l | l | l | l | l | l | l | l | l | l | l | l | l | l |
| 0.551 | 14.0 | l | l | l | l | l | l | l | l | l | l | l | l | l | l | ||||
| 0.630 | 16.0 | l | l | l | l | l | l | l | l | l | l | l | l | l | l | ||||
| 0.689 | 17.5 | l | l | l | l | l | l | l | l | l | l | ||||||||
| 0.748 | 19.0 | l | l | l | l | l | l | l | l | ||||||||||
| 0.787 | 20.0 | l | l | l | l | l | l | ||||||||||||