RVS plaat
310/310S roestfrij stiel plaat
310 RVS austenitic chromium nikkel RVS hat goede oksidaasje ferset, corrosie ferset, omdat it hegere persintaazje fan Chromium en nikkel, 310 hat folle bettere krûp sterkte, kin kontinu wurkje ûnder hege temperatuer, goede waarmte ferset.
310S RVS is austenitic chromium nikkel RVS, hat in goede 310S RVS oksidaasje ferset, ferset Corrosive.
De ferskillen fan gemyske gearstalling foar 310/310S roestvrij stiel
| Klasse | C(%) | Si(%) | Mn(%） | P(%) | S(%） | Cr(%) | Ni(%) | N(%) | Cu(%) |
| 310 | ≤0,25 | ≤1.0 | ≤2.0 | ≤0,03 | --- | 24.0-26.0 | 19.0-22.0 | --- | --- |
| 310S | ≤0,08 | ≤1.0 | ≤2.0 | ≤0,03 | ≤0,03 | 24.0-26.0 | 19.0-22.0 | --- | --- |
De ferskillen fan meganyske eigendom foar 310/310S RVS
| Klasse | treksterkteMpa | Yield sterkteMpa | Ferlinging(%) | taryf fan reduksje yn gebiet(%) | Tichtheid(g/cm3) |
| 310 | ≥470 | ≥17 | ≥40 | ≥50 | 7.98 |
| 310S | ≥520 | ≥205 | ≥40 | ≥50 | 7.98 |
304/304L/304H roestfrij blêd
Oer 304 materiaal:304 RVS is in mienskiplik RVS materiaal, de tichtheid fan 7,93 g / cm3, de yndustry wurdt ek neamd 18/8 RVS.Hege temperatuerresistinsje fan 800 graden, mei goede ferwurkingsprestaasjes, skaaimerken fan hege taaiens, in soad brûkt yn yndustriële en meubeldekoraasje-yndustry en fiedingsindustry.
Oer 304L materiaal:304L stiel as in lege C yn 'e algemiene steat, syn corrosie ferset en 304 ferlykbere, mar nei welding of stress nei syn treflike corrosie ferset oan it nôt grins.Yn it gefal sûnder waarmte behanneling, kin bliuwe goede corrosie ferset, algemien brûke 400 of minder (net-magnetysk, temperatuer -196 graden Celsius oant 800 graden Celsius).In soad brûkt foar it produsearjen fan goede algemiene prestaasjeseasken (korrosjebestriding en formabiliteit) fan apparatuer en dielen.
Oer 304H materiaal:304H is in soarte fan RVS, mei goede bûgen, welding proses prestaasjes, corrosie ferset, hege duorsumens en organisatoaryske stabiliteit, kâld deformation fermogen is hiel goed.De heechste temperatuer kin berikke 650 DEG C, en de oksidaasje ferset is oant 850 DEG C
De ferskillen fan gemyske gearstalling foar 304 304L 304H
| Klasse | C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Ni(%) | N(%) | |
| 304 | ≤0,08 | ≤0,75 | ≤2.0 | ≤0,045 | ≤0,03 | 18.0-20.0 | 8.0-10.5 | ≤0.1 | |
| 304L | ≤0,03 | ≤0,75 | ≤2.0 | ≤0,045 | ≤0,03 | 18.0-20.0 | 8.0-12.0 | ≤0.1 | |
| 304H | 0.04-1.0 | ≤0,75 | ≤2.0 | ≤0,045 | ≤0,03 | 18.0-20.0 | 8.0-10.5 | ---- | |
De ferskillen fan Mechanical eigendom foar 304 304L 304H
| Klasse | treksterkte(Mpa) | Yield sterkte(Mpa) | Ferlinging(%) | Hurdens(HR) |
| 304 | ≥515 | ≥205 | ≥40 | ≥92 |
| 304L | ≥485 | ≥170 | ≥40 | ≥92 |
| 304H | ≥515 | ≥205 | ≥40 | ≥92 |
316/316L roestfrij stiel plaat
Oer 316 materiaal:316 RVS troch tafoegjen Mo elemint, de corrosie ferset, en hege temperatuer sterkte is gâns ferbettere, hege temperatuer kin berikke 1200-1300 graden, kin brûkt wurde yn swiere conditions.Corrosion ferset is better as 304 RVS, yn pulp en papier produksje proses hat goede corrosie ferset.En 316 RVS is ek resistint foar eroazje fan marine en corrosive yndustriële sfear.
Oer 316L materiaal:316L RVS hat in koalstof ynhâld fan minder as 316, dat wurdt faak brûkt yn pulp en papier apparatuer waarmtewikselers, fervjen apparatuer, film waskjen apparatuer, pipelines, kustgebieten bûten de boumaterialen.Corrosie ferset is better as 316 materiaal.
De ferskillen fan gemyske gearstalling foar 316 316L RVS
| Klasse | C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Ni(%) | Mo(%) | Cu(%) |
| 316 | ≤0,08 | ≤1.0 | ≤2.0 | ≤0,045 | ≤0,03 | 16.0-18.0 | 10.0-14.0 | 2.0-3.0 | |
| 316L | ≤0,03 | ≤1.0 | ≤2.0 | ≤0,045 | ≤0,03 | 16.0-18.0 | 10.0-14.0 | 2.0-3.0 |
De ferskillen fan Mechanical eigendom foar 316 316L RVS
| Klasse | treksterkteMpa | Yield sterkteMpa | Ferlinging(%) | taryf fan reduksje yn gebiet(%) | Tichtheid(g/cm3) |
| 316 | ≥520 | ≥205 | ≥40 | ≥60 | 7.98 |
| 316L | ≥480 | ≥177 | ≥40 | ≥60 | 7.98 |
430 roestfrij stiel sheet
430 RVS is in goede corrosie ferset fan gewoane stiel, termyske prestaasjes as austenitic goed, termyske útwreiding koeffizient as austenitic lyts, waarmte wurgens, add stabilisaasje elemint titanium, weld dielen meganyske prestaasjes is goed.
430 roestfrij stiel brûkt yn arsjitektoanysk gebrûk, dielen fan brânstofbrenners, húshâldlike apparaten, dielen fan húshâldlike apparaten.
Gemyske gearstalling foar 430 roestvrij stiel
| Klasse | C(%) | Mn(%) | Si(%) | P(%) | S(%) | Cr(%) | Ni(%) | Mo(%) | Cu(%) |
| 430 | ≤0.12 | ≤1.0 | ≤0,75 | ≤0,04 | ≤0,03 | 16.0-18.0 | ≤0,06 | --- | --- |
Mechanysk eigendom foar 430 roestfrij stiel
| Klasse | treksterkteMpa | Yield sterkteMpa | Ferlinging(%) | taryf fan reduksje yn gebiet(%) | Tichtheid(g/cm3) |
| 430 | ≥450 | ≥205 | ≥22 | --- | 7.75 |
| Klasse | Ein | Dikte (mm) | Breedte (mm) | Lengte (mm) |
| 310 | 2B / No.4 / HL / BA / Mirror etc | 0.4mm-0.3mm | Standert breedte yn Sina: 1000mm 1219mm 1500mm | |
| 310s | No.1 | 3.0mm-80.0mm | Standert breedte yn Sina: 1219mm 1500mm 2000mm | |
| 304 | 2b, nr.4 PE | 0,55 | 914, 1219 | 1828, 2438 |
| 304 | 2B, No. 4 PE | 0,70 | 914, 1219 | 1828, 2438 |
| 304 | 2B, 2B PE, No. 4 PE, BA PE | 0,90 | 914, 1219 | 1828, 2438 |
| 304 | 2B, 2B PE, No. 4 PE, BA PE | 1.20 | 914, 1219, 1500 | 1828, 2438, 3000, 3048, 3658 |
| 304 | 2B, 2B PE, No. 4 PE | 1,50 | 914, 1219, 1500 | 1828, 2438, 3000, 3048, 3658 |
| 304 | 2B, 2B PE, No. 4 PE | 1.60 | 914, 1219, 1500 | 1828, 2438, 3000, 3048, 3658 |
| 304 | 2B, 2B PE, No. 4 PE | 2.00 | 914, 1219, 1500 | 1828, 2438, 3000, 3048, 3658 |
| 304 | 2B, 2B PE, No. 4 PE | 2,50 | 914, 1219, 1500 | 1828, 2438, 3000, 3048, 3658 |
| 304 | 2B, 2B PE, No. 4 PE | 3.00 | 914, 1219, 1500 | 1828, 2438, 3000, 3048, 3658 |
| 304L | 2B, 2B PE | 4.00 | 1500, 2000 | 3000, 6000 |
| 304H | 2B / No.4 / HL / BA / Mirror etcNo.1 | 3.00 | 1219, 1500,2000 | |
| 310 | 2B / No.4 / HL / BA / | 0,4-0,3 | 1000,1219,1500 | |
| 310s | No.1 | 3.00 | 1219, 1500,2000 | |
| 316 | 2B | 0,55 | 1219 | 2438 |
| 316 | 2B | 0,70 | 1219 | 2438 |
| 316 | 2B | 0,90 | 1219 | 2438 |
| 316 | 2b, nr.4 PE | 1.20 | 1219 | 2438 |
| 316 | 2b, nr.4 PE | 1,50 | 1219, 1500 | 2438, 3000, 3658 |
| 316 | 2b, nr.4 PE | 1.60 | 1219, 1500 | 2438, 3000, 3658 |
| 316 | 2b, nr.4 PE | 2.00 | 1219, 1500 | 2438, 3000, 3658 |
| 316 | 2b, nr.4 PE | 2,50 | 1219, 1500 | 2438, 3000, 3658 |
| 316 | 2b, nr.4 PE | 3.00 | 1219, 1500 | 2438, 3000, 3658 |
| 316L | 2B, 2B PE | 4.00 | 1500, 2000 | 3000, 6000 |
| 430 | BA PE, No. 4 PE | 0,70 | 914, 1219 | 1828, 2438 |
| 430 | BA PE, No. 4 PE | 0,90 | 914, 1219 | 1828, 2438 |
| 3CR12 | 2B | 1.2 | 1250 | 2500 |
| 3CR12 | 2B | 1.6 | 1250 | 2500 |
| 3CR12 | 2B | 2.0 | 1250 | 2500 |
| 3CR12 | Nûmer 1 | 4.0 | 1250, 1500 | 2500, 3000, 6000 |
Oare graden en breedtes
Graden: 301L, 310, 321, 2205, 253MA.
Breedten (mm): 600, 750, 900, 1050, 1200, 1524.
310/310S roestfrij stiel plaat
| Klasse | GB/T 1220-2007 | ASTM | DIN | JIS | KS |
| 310 | 20Cr25Ni20 | 310 | 1.4821 | SUS310 | STS310 |
| 310S | 06Cr25Ni20 | 310S | 1.4845 | SUS310S | STS310S |
Noarmen foar 304 304L 304H roestvrij stiel
| Klasse | GB/T 1220-2007 | ASTM | DIN | JIS | KS |
| 304 | 06Cr19Ni10 | 304 | 1.4301 | SUS304 | STS304 |
| 304L | 022Cr19Ni10 | 304L | 1.4306 | SUS304L | STS304L |
| 304H | —- | 304H | —- | SUS304H | STS304H |
Noarmen foar 316/316L RVS
| Klasse | GB/T 1220-2007 | ASTM | DIN | JIS | KS |
| 316 | 06Cr17Ni12Mo2 | 316 | 1.4401 | SUS316 | STS316 |
| 316L | 022Cr17Ni12Mo | 316L | 1.4404 | SUS316L | STS316L |
Noarmen foar430rustfrij stiel
| Klasse | GB | ASTM | DIN | JIS |
| 316 | 10 kr17 | 430 | 1.4016 | SUS430 |
| Dikte | Austenityske nominale massa (kg/m²) | Ferrityske nominale massa (kg/m²) |
| 0,45 | 3.68 | |
| 0,55 | 4,50 | |
| 0,70 | 5.72 | |
| 0,90 | 7.36 | |
| 1.20 | 9.81 | 9.61 |
| 1,50 | 12.3 | |
| 1.60 | 13.08 | 12.85 |
| 2.00 | 16.35 | 16.02 |
| 2,50 | 20.44 | 20.03 |
| 3.00 | 24.53 | 24.04 |
| 4.00 | 32.71 | 32.06 |
| Oerflakte ôfwurking | Definysje | Oanfraach |
| 2B | Dy klear, nei kâld rôljen, troch waarmte behanneling, pickling of oare lykweardige behanneling en as lêste troch kâld rôljen ta jûn passende glâns. | Medyske apparatuer, Food yndustry, Bou materiaal, Keukengerei. |
| BA | Dy ferwurke mei heldere waarmte behanneling nei kâld rolling. | Keukengerei, Elektryske apparatuer, Bouwkonstruksje. |
| NO.3 | Dy klear troch polishing mei No.100 oan No.120 abrasives oantsjutte yn JIS R6001. | Keukengerei, Bouwkonstruksje. |
| NO.4 | Dy klear troch polishing mei No.150 oan No.180 abrasives oantsjutte yn JIS R6001. | Keukengerei, Bouwkonstruksje, Medyske apparatuer. |
| HL | Dy klear polishing sa as te jaan trochgeande polishing strepen troch mei help fan abrasive fan geskikt nôt grutte. | Boukonstruksje. |
| NO.1 | It oerflak ôfmakke troch waarmte behanneling en pickling of prosessen oerienkommende dêr nei hot rolling. | Chemical tank, pipe. |
| No.8 | Heech reflektearjende 'spegel' finish.Produsearre fan 2B-finish troch polijsten mei opienfolgjende fynere abrasives folge troch wiidweidich buffing.Benammen brûkt yn arsjitektoanyske tapassingen. | |
| Klant-spesifike | Heech reflektearjende 'spegel' finish.Produsearre fan 2B-finish troch polijsten mei opienfolgjende fynere abrasives folge troch wiidweidich buffing.Benammen brûkt yn arsjitektoanyske tapassingen. |