Plak asye pur
310/ 310S fèy asye pur
310 asye pur austenitic chromium nikèl asye pur gen bon rezistans oksidasyon, rezistans korozyon, paske pousantaj ki pi wo nan chromium ak nikèl, 310 gen pi bon fòs ranpe, ka kontinyèlman travay anba tanperati ki wo, bon rezistans chalè.
310S Nerjaveèi asye se austenitic chromium nikèl Nerjaveèi asye, gen yon bon 310S Nerjaveèi asye oksidasyon rezistans, rezistans korozivite.
Diferans ki genyen nan konpozisyon chimik pou asye pur 310/310S
| Klas | C(%) | Si(%) | Mn(%） | P（%） | S(%） | Cr(%) | Ni(%) | N(%) | Cu(%) |
| 310 | ≤0.25 | ≤1.0 | ≤2.0 | ≤0.03 | --- | 24.0-26.0 | 19.0-22.0 | --- | --- |
| 310S | ≤0.08 | ≤1.0 | ≤2.0 | ≤0.03 | ≤0.03 | 24.0-26.0 | 19.0-22.0 | --- | --- |
Diferans ki genyen nan pwopriyete mekanik pou 310/310S asye pur
| Klas | fòs ruptureMpa | Sede fòsMpa | Elongasyon(%) | pousantaj rediksyon nan zòn nan(%) | Dansite(g/cm3) |
| 310 | ≥470 | ≥17 | ≥40 | ≥50 | 7.98 |
| 310S | ≥520 | ≥205 | ≥40 | ≥50 | 7.98 |
304/ 304L/ 304H Nerjaveèi fèy
Apeprè 304 materyèl:304 Nerjaveèi asye se yon materyèl komen Nerjaveèi, dansite a nan 7.93 g / cm3, se endistri a yo rele tou 18/8 Nerjaveèi asye.Rezistans tanperati ki wo nan 800 degre, ak bon pèfòmans pwosesis, karakteristik severite segondè, lajman ki itilize nan endistri dekorasyon endistriyèl ak mèb ak endistri manje.
Apeprè 304L materyèl:304L asye kòm yon C ki ba nan eta jeneral la, rezistans korozyon li yo ak 304 menm jan an, men apre yo fin soude oswa estrès apre ekselan rezistans korozyon li yo nan fwontyè grenn jaden an.Nan ka a san tretman chalè, ka rete bon rezistans korozyon, jeneralman itilize 400 oswa mwens (ki pa mayetik, tanperati -196 degre Sèlsiyis a 800 degre Sèlsiyis).Lajman itilize yo pwodwi bon kondisyon pèfòmans jeneral (rezistans korozyon ak fòmabilite) nan ekipman ak pati.
Apeprè 304H materyèl:304H se yon kalite asye pur, ak bon koube, pèfòmans pwosesis soude, rezistans korozyon, rezistans segondè ak estabilite òganizasyonèl, kapasite deformation frèt trè bon.Tanperati ki pi wo a ka rive nan 650 DEG C, ak rezistans nan oksidasyon se jiska 850 DEG C
Diferans ki genyen nan konpozisyon chimik pou 304 304L 304H
| Klas | C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Ni(%) | N(%) | |
| 304 | ≤0.08 | ≤0.75 | ≤2.0 | ≤0.045 | ≤0.03 | 18.0-20.0 | 8.0-10.5 | ≤0.1 | |
| 304L | ≤0.03 | ≤0.75 | ≤2.0 | ≤0.045 | ≤0.03 | 18.0-20.0 | 8.0-12.0 | ≤0.1 | |
| 304H | 0.04-1.0 | ≤0.75 | ≤2.0 | ≤0.045 | ≤0.03 | 18.0-20.0 | 8.0-10.5 | ---- | |
Diferans ki genyen nan pwopriyete mekanik pou 304 304L 304H
| Klas | fòs rupture(Mpa) | Sede fòs(Mpa) | Elongasyon(%) | Dite(HR) |
| 304 | ≥515 | ≥205 | ≥40 | ≥92 |
| 304L | ≥485 | ≥170 | ≥40 | ≥92 |
| 304H | ≥515 | ≥205 | ≥40 | ≥92 |
316/ 316L fèy asye pur
Apeprè 316 materyèl:316 Nerjaveèi lè yo ajoute Mo eleman, rezistans korozyon an, ak fòs tanperati ki wo anpil amelyore, tanperati ki wo ka rive nan 1200-1300 degre, yo ka itilize nan kondisyon grav. Rezistans korozyon pi bon pase 304 asye pur, nan pwodiksyon kaka ak papye. pwosesis gen bon rezistans korozyon.Ak 316 asye pur se tou rezistan a ewozyon nan atmosfè marin ak korozivite endistriyèl.
Apeprè 316L materyèl:316L Nerjaveèi gen yon kontni kabòn ki mwens pase 316, ki se souvan itilize nan kaka ak echanjeur chalè ekipman papye, ekipman DYEING, ekipman lave fim, tiyo, zòn kotyè deyò materyèl bilding yo.Rezistans korozyon pi bon pase 316 materyèl.
Diferans ki genyen nan konpozisyon chimik pou 316 316L asye pur
| Klas | C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Ni(%) | Mo(%) | Cu(%) |
| 316 | ≤0.08 | ≤1.0 | ≤2.0 | ≤0.045 | ≤0.03 | 16.0-18.0 | 10.0-14.0 | 2.0-3.0 | |
| 316L | ≤0.03 | ≤1.0 | ≤2.0 | ≤0.045 | ≤0.03 | 16.0-18.0 | 10.0-14.0 | 2.0-3.0 |
Diferans ki genyen nan pwopriyete mekanik pou 316 316L asye pur
| Klas | fòs ruptureMpa | Sede fòsMpa | Elongasyon(%) | pousantaj rediksyon nan zòn nan(%) | Dansite(g/cm3) |
| 316 | ≥520 | ≥205 | ≥40 | ≥60 | 7.98 |
| 316L | ≥480 | ≥177 | ≥40 | ≥60 | 7.98 |
430 fèy asye pur
430 Nerjaveèi asye se yon bon rezistans korozyon nan asye komen, pèfòmans tèmik pase austenitic bon, koyefisyan ekspansyon tèmik pase austenitic ti, fatig chalè, ajoute estabilizasyon eleman Titàn, soude pati pèfòmans mekanik se yon bon bagay.
430 Nerjaveèi yo itilize nan itilizasyon achitekti, pati brûler gaz, aparèy nan kay la, pati aparèy nan kay la.
Konpozisyon chimik pou 430 asye pur
| Klas | C(%) | Mn(%) | Si(%) | P(%) | S(%) | Cr(%) | Ni(%) | Mo(%) | Cu(%) |
| 430 | ≤0.12 | ≤1.0 | ≤0.75 | ≤0.04 | ≤0.03 | 16.0-18.0 | ≤0.06 | --- | --- |
Pwopriyete mekanik pou 430 asye pur
| Klas | fòs ruptureMpa | Sede fòsMpa | Elongasyon(%) | pousantaj rediksyon nan zòn nan(%) | Dansite(g/cm3) |
| 430 | ≥450 | ≥205 | ≥22 | --- | 7.75 |
| Klas | Fini | Epesè (mm) | Lajè (mm) | Longè (mm) |
| 310 | 2B / No.4 / HL / BA / glas elatriye | 0.4mm-0.3mm | Estanda lajè nan Lachin: 1000mm 1219mm 1500mm | |
| 310s | No.1 | 3.0mm-80.0mm | Estanda lajè nan Lachin: 1219mm 1500mm 2000mm | |
| 304 | 2B, Non.4 PE | 0.55 | 914, 1219 | 1828, 2438 |
| 304 | 2B, nimewo 4 PE | 0.70 | 914, 1219 | 1828, 2438 |
| 304 | 2B, 2B PE, No 4 PE, BA PE | 0.90 | 914, 1219 | 1828, 2438 |
| 304 | 2B, 2B PE, No 4 PE, BA PE | 1.20 | 914, 1219, 1500 | 1828, 2438, 3000, 3048, 3658 |
| 304 | 2B, 2B PE, nimewo 4 PE | 1.50 | 914, 1219, 1500 | 1828, 2438, 3000, 3048, 3658 |
| 304 | 2B, 2B PE, nimewo 4 PE | 1.60 | 914, 1219, 1500 | 1828, 2438, 3000, 3048, 3658 |
| 304 | 2B, 2B PE, nimewo 4 PE | 2.00 | 914, 1219, 1500 | 1828, 2438, 3000, 3048, 3658 |
| 304 | 2B, 2B PE, nimewo 4 PE | 2.50 | 914, 1219, 1500 | 1828, 2438, 3000, 3048, 3658 |
| 304 | 2B, 2B PE, nimewo 4 PE | 3.00 | 914, 1219, 1500 | 1828, 2438, 3000, 3048, 3658 |
| 304L | 2B, 2B PE | 4.00 | 1500, 2000 | 3000, 6000 |
| 304H | 2B / No.4 / HL / BA / glas elatriyeNo.1 | 3.00 | 1219, 1500,2000 | |
| 310 | 2B / No.4 / HL / BA / | 0.4-0.3 | 1000,1219,1500 | |
| 310s | No.1 | 3.00 | 1219, 1500,2000 | |
| 316 | 2B | 0.55 | 1219 | 2438 |
| 316 | 2B | 0.70 | 1219 | 2438 |
| 316 | 2B | 0.90 | 1219 | 2438 |
| 316 | 2B, Non.4 PE | 1.20 | 1219 | 2438 |
| 316 | 2B, Non.4 PE | 1.50 | 1219, 1500 | 2438, 3000, 3658 |
| 316 | 2B, Non.4 PE | 1.60 | 1219, 1500 | 2438, 3000, 3658 |
| 316 | 2B, Non.4 PE | 2.00 | 1219, 1500 | 2438, 3000, 3658 |
| 316 | 2B, Non.4 PE | 2.50 | 1219, 1500 | 2438, 3000, 3658 |
| 316 | 2B, Non.4 PE | 3.00 | 1219, 1500 | 2438, 3000, 3658 |
| 316L | 2B, 2B PE | 4.00 | 1500, 2000 | 3000, 6000 |
| 430 | BA PE, No 4 PE | 0.70 | 914, 1219 | 1828, 2438 |
| 430 | BA PE, No 4 PE | 0.90 | 914, 1219 | 1828, 2438 |
| 3CR12 | 2B | 1.2 | 1250 | 2500 |
| 3CR12 | 2B | 1.6 | 1250 | 2500 |
| 3CR12 | 2B | 2.0 | 1250 | 2500 |
| 3CR12 | nimewo 1 | 4.0 | 1250, 1500 | 2500, 3000, 6000 |
Lòt klas ak lajè
Klas: 301L, 310, 321, 2205, 253MA.
Lajè (mm): 600, 750, 900, 1050, 1200, 1524.
310/ 310S fèy asye pur
| Klas | GB/T 1220-2007 | ASTM | DIN | JIS | KS |
| 310 | 20Cr25Ni20 | 310 | 1.4821 | SUS310 | STS310 |
| 310S | 06Cr25Ni20 | 310S | 1.4845 | SUS310S | STS310S |
Estanda pou 304 304L 304H asye pur
| Klas | GB/T 1220-2007 | ASTM | DIN | JIS | KS |
| 304 | 06Cr19Ni10 | 304 | 1.4301 | SUS304 | STS304 |
| 304L | 022Cr19Ni10 | 304L | 1.4306 | SUS304L | STS304L |
| 304H | —- | 304H | —- | SUS304H | STS304H |
Estanda pou 316/316L asye pur
| Klas | GB/T 1220-2007 | ASTM | DIN | JIS | KS |
| 316 | 06Cr17Ni12Mo2 | 316 | 1.4401 | SUS316 | STS316 |
| 316L | 022Cr17Ni12Mo | 316L | 1.4404 | SUS316L | STS316L |
Estanda pou430asye pur
| Klas | GB | ASTM | DIN | JIS |
| 316 | 10Cr17 | 430 | 1.4016 | SUS430 |
| Epesè | Mas nominal austenitic (kg/m²) | Mas nominal feritik (kg/m²) |
| 0.45 | 3.68 | |
| 0.55 | 4.50 | |
| 0.70 | 5.72 | |
| 0.90 | 7.36 | |
| 1.20 | 9.81 | 9.61 |
| 1.50 | 12.3 | |
| 1.60 | 13.08 | 12.85 |
| 2.00 | 16.35 | 16.02 |
| 2.50 | 20.44 | 20.03 |
| 3.00 | 24.53 | 24.04 |
| 4.00 | 32.71 | 32.06 |
| Sifas fini | Definisyon | Aplikasyon |
| 2B | Moun ki fini, apre woule frèt, pa tretman chalè, marinated oswa lòt tretman ekivalan epi anfen pa woule frèt bay ekla apwopriye. | Ekipman medikal, endistri manje, materyèl konstriksyon, istansil kwizin. |
| BA | Moun ki trete ak tretman chalè klere apre woule frèt. | Ustensile kwizin, ekipman elektrik, konstriksyon bilding. |
| NO.3 | Moun ki fini pa polisaj ak No.100 a No.120 abrazif espesifye nan JIS R6001. | Veso kizin, konstriksyon bilding. |
| NO.4 | Moun ki fini pa polisaj ak No.150 a No.180 abrazif espesifye nan JIS R6001. | Ustensile kwizin, konstriksyon bilding, ekipman medikal. |
| HL | Moun sa yo ki fini polisaj konsa yo bay tach polisaj kontinyèl lè l sèvi avèk abrazif nan gwosè grenn ki apwopriye. | Konstriksyon bilding. |
| NO.1 | Sifas la fini pa tretman chalè ak marinated oswa pwosesis ki koresponn gen apre woule cho. | Tank chimik, tiyo. |
| No.8 | Trè reflektif 'glas' fini.Pwodui soti nan 2B fini pa polisaj ak abrazif siksesif pi rafine swiv pa anpil polisaj.Sitou itilize nan aplikasyon achitekti. | |
| Espesifik kliyan | Trè reflektif 'glas' fini.Pwodui soti nan 2B fini pa polisaj ak abrazif siksesif pi rafine swiv pa anpil polisaj.Sitou itilize nan aplikasyon achitekti. |