Bamba la chuma cha pua |

Sahani ya chuma cha pua

Maelezo Fupi:

Maneno muhimu (aina ya bomba):Bamba la Chuma cha pua, karatasi ya chuma cha pua, karatasi ya chuma

Ukubwa:Laha(0.2mm-4mm), Slab(4mm-20mm), Sahani Nene(20mm-60mm), Sahani maalum nene(60-115mm)

Uvumilivu:Kipenyo cha Nje:6-32mm:+/- 0.2mm, 32-38:+/-0.15mm,42-60:+/-0.20mm,60mm:+/-0.25mm b) Unene: +/- 10% c ) Urefu: +/- 5mm

Kiwango na Daraja:GB/T14976-2002, GB13296-91, GB9948-88, ASTM/ASME A213/SA213, ASTM/ASME A312/SA312, ASTM/ASME A269/SA269, DIN 17458-85,DIN 84IS6 JW 1545, DIN-154565, DIN-84565,656569 G 3463, JIS G 3448, JIS G 344

Mchakato wa Viwanda:Moto umevingirwa, moto umepanuliwa, baridi inayotolewa, na mabati ya moto

Uso:180G, 240G, 320G Satin / Hairline, 400G, 600G Mirror kumaliza

Ufungashaji:Karatasi interleaf, PE

Matumizi:Daraja la chuma, sahani ya kuchemsha, chuma cha kujenga meli, silaha za chuma, chuma cha gari, sahani ya paa, Chuma cha miundo, chuma cha umeme n.k.

Tutumie barua pepe Pakua kama PDF

Maelezo

Vipimo

Kawaida

Uso Maliza

Ufungashaji & upakiaji

310/310S karatasi ya chuma cha pua

310 chuma cha pua austenitic chromium nickel chuma cha pua ina nzuri oxidation upinzani, upinzani kutu, kwa sababu asilimia kubwa ya chromium na nikeli, 310 ina nguvu bora zaidi huenda, inaweza kuendelea kufanya kazi chini ya joto la juu, nzuri joto upinzani.

310S chuma cha pua ni austenitic chromium nickel chuma cha pua, ina nzuri 310S chuma cha pua oxidation upinzani, upinzani babuzi.

Tofauti za muundo wa kemikali kwa chuma cha pua cha 310/310S

Daraja	C(%)	Si(%)	Mn(%）	P(%)	S(%）	Cr(%)	Ni(%)	N(%)	Cu(%)
310	≤0.25	≤1.0	≤2.0	≤0.03	---	24.0-26.0	19.0-22.0	---	---
310S	≤0.08	≤1.0	≤2.0	≤0.03	≤0.03	24.0-26.0	19.0-22.0	---	---

Tofauti za mali ya Mitambo kwa 310/310S chuma cha pua

Daraja	nguvu ya mkazoMpa	Nguvu ya MavunoMpa	Kurefusha(%)	kiwango cha kupunguzwa kwa eneo(%)	Msongamano(g/cm3)
310	≥470	≥17	≥40	≥50	7.98
310S	≥520	≥205	≥40	≥50	7.98

304/ 304L/ 304H karatasi ya pua

Kuhusu nyenzo 304:304 chuma cha pua ni nyenzo ya kawaida ya chuma cha pua, wiani wa 7.93 g/cm3, sekta hiyo pia inaitwa 18/8 chuma cha pua.Upinzani wa joto la juu la digrii 800, na utendaji mzuri wa usindikaji, sifa za juu za ushupavu, zinazotumiwa sana katika tasnia ya viwanda na mapambo ya fanicha na tasnia ya chakula.

Kuhusu nyenzo 304L:304L chuma kama C ya chini katika hali ya jumla, upinzani ulikaji wake na 304 sawa, lakini baada ya kulehemu au mkazo baada ya upinzani wake bora ulikaji kwa mpaka nafaka.Katika kesi bila matibabu ya joto, inaweza kubaki nzuri ulikaji upinzani, kwa ujumla kutumia 400 au chini (yasiyo ya magnetic, joto -196 digrii Celsius hadi 800 digrii Celsius).Inatumika sana kuzalisha mahitaji mazuri ya utendaji wa jumla (upinzani wa kutu na uundaji) wa vifaa na sehemu.

Kuhusu nyenzo za 304H:304H ni aina ya chuma cha pua, na bending nzuri, utendaji mchakato wa kulehemu, upinzani kutu, uimara juu na utulivu wa shirika, baridi deformation uwezo ni nzuri sana.Joto la juu zaidi linaweza kufikia 650 ° C, na upinzani wa oxidation ni hadi 850 DEG C.

Tofauti za muundo wa Kemikali kwa 304 304L 304H

Daraja	C(%)	Si(%)	Mn(%)	P(%)	S(%)	Cr(%)		Ni(%)	N(%)
304	≤0.08	≤0.75	≤2.0	≤0.045	≤0.03	18.0-20.0		8.0-10.5	≤0.1
304L	≤0.03	≤0.75	≤2.0	≤0.045	≤0.03	18.0-20.0	8.0-12.0		≤0.1
304H	0.04-1.0	≤0.75	≤2.0	≤0.045	≤0.03	18.0-20.0		8.0-10.5	----

Tofauti za Mali ya Mitambo kwa 304 304L 304H

Daraja	nguvu ya mkazo(Mpa)	Nguvu ya Mavuno(Mpa)	Kurefusha(%)	Ugumu(HR)
304	≥515	≥205	≥40	≥92
304L	≥485	≥170	≥40	≥92
304H	≥515	≥205	≥40	≥92

316/316L karatasi ya chuma cha pua

Kuhusu nyenzo 316:316 chuma cha pua kwa kuongeza kipengele cha Mo, upinzani wa kutu, na nguvu ya joto la juu imeongezeka sana, joto la juu linaweza kufikia digrii 1200-1300, linaweza kutumika katika hali kali. Upinzani wa kutu ni bora kuliko 304 chuma cha pua, katika uzalishaji wa massa na karatasi. mchakato una upinzani mzuri wa kutu.Na 316 chuma cha pua pia ni sugu kwa mmomonyoko wa anga ya baharini na babuzi ya viwanda.

Kuhusu nyenzo 316L:316L chuma cha pua ina maudhui ya kaboni ya chini ya 316, ambayo hutumiwa kwa kawaida katika kubadilishana joto la massa na karatasi, vifaa vya dyeing, vifaa vya kuosha filamu, mabomba, maeneo ya pwani nje ya vifaa vya ujenzi.Upinzani wa kutu ni bora kuliko nyenzo 316.

Tofauti za muundo wa kemikali kwa 316 316L chuma cha pua

Daraja	C(%)	Si(%)	Mn(%)	P(%)	S(%)	Cr(%)	Ni(%)	Mo(%)	Cu(%)
316	≤0.08	≤1.0	≤2.0	≤0.045	≤0.03	16.0-18.0	10.0-14.0	2.0-3.0
316L	≤0.03	≤1.0	≤2.0	≤0.045	≤0.03	16.0-18.0	10.0-14.0	2.0-3.0

Tofauti za mali ya Mitambo kwa 316 316L chuma cha pua

Daraja	nguvu ya mkazoMpa	Nguvu ya MavunoMpa	Kurefusha(%)	kiwango cha kupunguzwa kwa eneo(%)	Msongamano(g/cm3)
316	≥520	≥205	≥40	≥60	7.98
316L	≥480	≥177	≥40	≥60	7.98

430 karatasi ya chuma cha pua

430 chuma cha pua ni nzuri ulikaji upinzani wa chuma ya kawaida, utendaji mafuta kuliko austenitic nzuri, mafuta upanuzi mgawo kuliko austenitic ndogo, joto uchovu, kuongeza utulivu kipengele titanium, weld sehemu ya utendaji wa mitambo ni nzuri.

430 chuma cha pua kinachotumika katika matumizi ya usanifu, sehemu za kuchoma mafuta, vifaa vya nyumbani, sehemu za vifaa vya nyumbani.

Muundo wa kemikali kwa chuma cha pua 430

Daraja	C(%)	Mn(%)	Si(%)	P(%)	S(%)	Cr(%)	Ni(%)	Mo(%)	Cu(%)
430	≤0.12	≤1.0	≤0.75	≤0.04	≤0.03	16.0-18.0	≤0.06	---	---

Mali ya mitambo kwa chuma cha pua 430

Daraja	nguvu ya mkazoMpa	Nguvu ya MavunoMpa	Kurefusha(%)	kiwango cha kupunguzwa kwa eneo(%)	Msongamano(g/cm3)
430	≥450	≥205	≥22	---	7.75

Iliyotangulia: Kipunguzaji

Inayofuata: Pamoja ya Pup

Daraja	Maliza	Unene (mm)	Upana (mm)	Urefu (mm)
310	2B / No.4 / HL / BA / Mirror nk	0.4mm-0.3mm	Upana wa kawaida nchini China: 1000mm 1219mm 1500mm
310s	No.1	3.0mm-80.0mm	Upana wa kawaida nchini China: 1219mm 1500mm 2000mm
304	2B, Hapana.4 PE	0.55	914, 1219	1828, 2438
304	2B, Nambari 4 PE	0.70	914, 1219	1828, 2438
304	2B, 2B PE, No. 4 PE, BA PE	0.90	914, 1219	1828, 2438
304	2B, 2B PE, No. 4 PE, BA PE	1.20	914, 1219, 1500	1828, 2438, 3000, 3048, 3658
304	2B, 2B PE, No. 4 PE	1.50	914, 1219, 1500	1828, 2438, 3000, 3048, 3658
304	2B, 2B PE, No. 4 PE	1.60	914, 1219, 1500	1828, 2438, 3000, 3048, 3658
304	2B, 2B PE, No. 4 PE	2.00	914, 1219, 1500	1828, 2438, 3000, 3048, 3658
304	2B, 2B PE, No. 4 PE	2.50	914, 1219, 1500	1828, 2438, 3000, 3048, 3658
304	2B, 2B PE, No. 4 PE	3.00	914, 1219, 1500	1828, 2438, 3000, 3048, 3658
304L	2B, 2B PE	4.00	1500, 2000	3000, 6000
304H	2B / No.4 /HL / BA / Mirror nkNo.1	3.00	1219, 1500,2000
310	2B / No.4 / HL / BA /	0.4-0.3	1000,1219,1500
310s	No.1	3.00	1219, 1500,2000
316	2B	0.55	1219	2438
316	2B	0.70	1219	2438
316	2B	0.90	1219	2438
316	2B, Hapana.4 PE	1.20	1219	2438
316	2B, Hapana.4 PE	1.50	1219, 1500	2438, 3000, 3658
316	2B, Hapana.4 PE	1.60	1219, 1500	2438, 3000, 3658
316	2B, Hapana.4 PE	2.00	1219, 1500	2438, 3000, 3658
316	2B, Hapana.4 PE	2.50	1219, 1500	2438, 3000, 3658
316	2B, Hapana.4 PE	3.00	1219, 1500	2438, 3000, 3658
316L	2B, 2B PE	4.00	1500, 2000	3000, 6000
430	BA PE, No. 4 PE	0.70	914, 1219	1828, 2438
430	BA PE, No. 4 PE	0.90	914, 1219	1828, 2438
3CR12	2B	1.2	1250	2500
3CR12	2B	1.6	1250	2500
3CR12	2B	2.0	1250	2500
3CR12	Nambari 1	4.0	1250, 1500	2500, 3000, 6000

Daraja zingine na upana

Madarasa: 301L, 310, 321, 2205, 253MA.

Upana (mm): 600, 750, 900, 1050, 1200, 1524.

310/310S karatasi ya chuma cha pua

Daraja	GB/T 1220-2007	ASTM	DIN	JIS	KS
310	20Cr25Ni20	310	1.4821	SUS310	STS310
310S	06Cr25Ni20	310S	1.4845	SUS310S	STS310S

Viwango vya 304 304L 304H chuma cha pua

Daraja	GB/T 1220-2007	ASTM	DIN	JIS	KS
304	06Cr19Ni10	304	1.4301	SUS304	STS304
304L	022Cr19Ni10	304L	1.4306	SUS304L	STS304L
304H	--	304H	--	SUS304H	STS304H

Viwango vya 316/316L chuma cha pua

Daraja	GB/T 1220-2007	ASTM	DIN	JIS	KS
316	06Cr17Ni12Mo2	316	1.4401	SUS316	STS316
316L	022Cr17Ni12Mo	316L	1.4404	SUS316L	STS316L

Viwango vya430chuma cha pua

Daraja	GB	ASTM	DIN	JIS
316	10Kr17	430	1.4016	SUS430

Unene	Uzito wa jina la Austenitic (kg/m²)	Uzito wa kawaida wa feri (kg/m²)
0.45	3.68
0.55	4.50
0.70	5.72
0.90	7.36
1.20	9.81	9.61
1.50	12.3
1.60	13.08	12.85
2.00	16.35	16.02
2.50	20.44	20.03
3.00	24.53	24.04
4.00	32.71	32.06

Uso Maliza	Ufafanuzi	Maombi
2B	Wale kumaliza, baada ya rolling baridi, kwa matibabu ya joto, pickling au matibabu mengine sawa na mwisho kwa rolling baridi kwa kupewa mwanga mwafaka.	Vifaa vya matibabu, Sekta ya chakula, Nyenzo za ujenzi, Vyombo vya jikoni.
BA	Wale kusindika na matibabu ya joto mkali baada ya rolling baridi.	Vyombo vya jikoni, Vifaa vya umeme, Ujenzi wa majengo.
NO.3	Zile zilimalizwa kwa kung'arisha na abrasives No.100 hadi No.120 zilizobainishwa katika JIS R6001.	Vyombo vya jikoni, Ujenzi wa majengo.
NO.4	Zile zilimalizwa kwa kung'arisha kwa abrasives No.150 hadi No.180 zilizobainishwa katika JIS R6001.	Vyombo vya jikoni, Ujenzi wa majengo, Vifaa vya matibabu.
HL	Wale waliomaliza kung'arisha ili kutoa michirizi inayoendelea ya kung'arisha kwa kutumia abrasive ya ukubwa unaofaa wa nafaka.	Ujenzi wa Jengo.
NO.1	Uso huo umekamilika kwa matibabu ya joto na kuokota au michakato inayolingana na baada ya kukunja moto.	Tangi ya kemikali, bomba.
Na.8	Mwisho wa 'kioo' unaoakisi sana.Imetolewa kutoka umaliziaji wa 2B kwa kung'arisha kwa abrasives bora zaidi zinazofuatana na kubofya kwa kina.Hasa kutumika katika maombi ya usanifu.
Mteja mahususi	Mwisho wa 'kioo' unaoakisi sana.Imetolewa kutoka umaliziaji wa 2B kwa kung'arisha kwa abrasives bora zaidi zinazofuatana na kubofya kwa kina.Hasa kutumika katika maombi ya usanifu.