Yintoni iIkhoneli 601?
I-Inconel 601 ilungele ukusetyenziswa kwizicelo ezifuna ubushushu obuphezulu obuphezulu kunye nokumelana nokukhula ukuya kuthi ga kwi-1100oC.Ngenxa yobukho be-nickel, i-alloy ixhathisa kakhulu kwi-oxidation ukuya kwi-2200oF okanye i-1250oC.Ivelisa umaleko weoksidi othembekileyo kakhulu ukunqanda ukuchitheka phantsi kwebhayisekile eshushu eshushu.Uzinzo oluphezulu lwe-metallurgical kunye ne-fine creep rupturing strength.Ithintela uphuhliso lwe-SIGMA kwaye ilungele ukusetyenziswa kwibhayisikile eshushu kunye nemisebenzi eyothusayo.
I-Super alloy 601 ineempawu ezilungileyo zoomatshini kumaqondo obushushu aphezulu.Amandla alungileyo aphunyezwa ngesisombululo esibandayo okanye ukuqiniswa kwemvula kwisiseko se-alloy.I-alloy igcina i-ductility entle nasemva kwenkonzo yexesha elide.Iyabumbeka ngokulula, iyacatshukiswa kwaye iyadityaniswa.
Iinkcukacha ze-Inconel 601
| Ucingo | Iphepha | Ukuhluba | Umbhobho | Intonga |
| ASTM B 166/ASME SB 166,DIN 17752, DIN 17753, DIN 17754, EN10095, ISO 9723,ISO 9724, ISO 9725, AWS A 5.14 ERNiCrFe-11 | ASTM B 168/ ASME SB 168 DIN 17750 EN10095, ISO 6208 | ASTM B 168/ ASME SB 168,DIN 17750 EN10095,ISO 6208 | I-ASTM B 167/ASME SB 167, ASTM B 751/ASME SB 751, ASTM B 775/ASME SB 775ASTM B 829/ASME SB 829, DIN 17751,ISO 6207 | ASTM B 166/ASME SB 166,DIN 17752,DIN 17753,DIN 17754,EN10095ISO 9723,ISO 9724,ISO 9725 |
I-Inconel 601 ukwakheka kweekhemikhali
| IiMfuno zeMichiza | |||||||
|
| Ni | Cr | C | Mn | Si | S | Fe |
| Max | 63.0 | 25.0 | 0.10 | 1.0 | 1.0 | 0.015 | UBhal |
| Min | 58.0 | 21.0 |
|
|
|
|
|
IPropati yoomatshini
| IiMfuno zePropati yoomatshini | |||||
|
| Ultimate Tensile | Amandla eSivuno (0.2% OS) | Elong.kwi-2 in., okanye 50mm okanye 4D, min., % | R/A | Ukuqina |
| Ukusebenza Okubandayo / Ukukhutshwa | |||||
| Min | 80 KSi | 30 KSi | 30 |
|
|
| Max |
|
|
|
|
|
| Min | 550 MPa | 205 MPa |
|
|
|
| Max |
|
|
|
|
|
| I-Hot Worked / i-Annealed | |||||
| Min | 80 KSi | 30 KSi | 30 |
|
|
| Max |
|
|
|
|
|
| Min | 550 MPa | 205 MPa |
|
|
|
| Max |
|
|
|
|
|
Piimpawu ze-hysical
| Ukuxinana | 8.11 Mg/m3 (0.293 lb/in3) |
| Uluhlu olunyibilikayo | 2480-2571°F (1360-1411°C) |
| Ubushushu obuthile | 70°F – 0.107 Btu/lb-°F (21°C – 448 J/kg-°C) |
| Permeability kwi 200 oersted |
|
| 76°F – 1.003 (24°C – 1.003) | |
| -109°F – 1.004 (-78°C – 1.004) | |
| -320°F – 1.016 (-196°C – 1.016) | |
| Ubushushu beCurie | <-320°F (<-196°C) |
Usetyenziso
l Ukusetyenziswa kobushushu obuphezulu kushishino lweemoto kunye ne-aerospace-i-rotors ye-turbocharger kunye ne-seals (ukusetyenziswa okuphawulekayo yi-Mazda RX-7 i-gen yesithathu), ii-injini ezijikelezayo (izithuthuthu zaseNorton), i-Formula 1 kunye ne-NASCAR exhaust systems;
l Ukusetyenziswa kobushushu obuphezulu kwi-aerospace-iibhleyidi zeinjini yegesi kunye nezangqa zokuvalela, izitywini kunye neziqhumiso, izitshizi ze-injini yejethi, iilitha ezitota ukutsha, kunye nezidibanisi ze-diffuser;
l Izixhobo zokulungisa i-Thermal-Iibhaskithi, iitreyi, kunye nezinto ezilungiselelwe ukubambisa, i-carburizing, i-carbonitriding, i-nitriding yokusetyenziswa kwe-industrial-heating, kunye nakwiityhubhu ezikhazimlayo, iimuffles, imbuyekezo, izikhuselo zedangatye, iityhubhu zokudibanisa imitya, amabhanti okuhambisa ngocingo olulukiweyo, kunye nezinto zokufudumeza umbane kwimizi-mveliso. iziko;
l Ukwenziwa kwemichiza-iinkonkxa zokukhusela kwi-ammonia reformers kunye nezixhobo zokuvelisa i-nitric acid;
l Ukwenziwa kwePetrochemical-iijenereyitha ze-catalyst kunye nezifudumezi zomoya;
l Ukusetyenziswa kolawulo longcoliseko-amagumbi okutsha kwizitshisi zenkunkuma eqinileyo;
l Indawo yokuvelisa amandla-I-superheater tube ixhasa imiqobo yegridi kunye nokuphathwa kothuthu
Ixesha lokuposa: Oct-14-2021