Ke engInconel 601?
Inconel 601 e loketse ho sebelisoa lits'ebetsong tse hlokang mocheso o phahameng ka ho fetesisa le ho hanyetsa kutu ho fihla ho 1100oC.Ka lebaka la boteng ba nickel, alloy e hanyetsana haholo le oxidation ho fihla ho 2200oF kapa 1250oC.E hlahisa oxide layer e tšepahalang haholo ho thibela spalling tlas'a libaesekele tse matla tsa mocheso.Botsitso bo phahameng ba metallurgical le matla a ho phunyeha a khahlehang.E qoba nts'etsopele ea SIGMA mme e loketse ho sebelisoa ts'ebetsong ea libaesekele tse futhumatsang le ts'ebetso e tšosang.
Super alloy 601 e na le thepa e ntle ea mochini mochesong o phahameng.Matla a matle a finyelloa ka tharollo e batang kapa ho matlafatsa pula holim'a motheo oa alloy.The alloy e boloka ductility e ntle esita le ka mor'a tšebeletso ea nako e telele.Ho bonolo ho theha, machinable le weldable.
Litlhaloso tsa Inconel 601
| Mohala | Leqephe | Hlobola | Pipe | Molamu |
| ASTM B 166/ASME SB 166,DIN 17752, DIN 17753, DIN 17754, EN10095, ISO 9723,ISO 9724, ISO 9725, AWS A 5.14 ERNiCrFe-11 | ASTM B 168/ ASME SB 168 DIN 17750 EN10095, ISO 6208 | ASTM B 168/ ASME SB 168,DIN 17750 EN10095,ISO 6208 | ASTM B 167/ASME SB 167, ASTM B 751/ASME SB 751, ASTM B 775/ASME SB 775ASTM B 829/ASME SB 829, DIN 17751,ISO 6207 | ASTM B 166/ASME SB 166,DIN 17752,DIN 17753,DIN 17754,EN10095ISO 9723,ISO 9724,ISO 9725 |
Inconel 601 sebopeho sa lik'hemik'hale
| Litlhoko tsa Lik'hemik'hale | |||||||
|
| Ni | Cr | C | Mn | Si | S | Fe |
| Max | 63.0 | 25.0 | 0.10 | 1.0 | 1.0 | 0.015 | Bal |
| Min | 58.0 | 21.0 |
|
|
|
|
|
Thepa ea Mechini
| Litlhoko tsa Thepa ea Mechini | |||||
|
| Ultimate Tensile | Matla a Kotulo (0.2% OS) | Elong.ho 2 in., kapa 50mm kapa 4D, min., % | R/A | Ho thatafala |
| Ba batang (ba-tla-tsa) /annealed | |||||
| Min | 80 KSi | 30 KSi | 30 |
|
|
| Max |
|
|
|
|
|
| Min | 550 MPa | 205 MPa |
|
|
|
| Max |
|
|
|
|
|
| Ho Sebetsa ka ho Chesa/Ho Annealed | |||||
| Min | 80 KSi | 30 KSi | 30 |
|
|
| Max |
|
|
|
|
|
| Min | 550 MPa | 205 MPa |
|
|
|
| Max |
|
|
|
|
|
Physical properties
| Botenya | 8.11 Mg/m3 (0.293 lb/in3) |
| Melting Range | 2480-2571°F (1360-1411°C) |
| Mocheso o khethehileng | 70°F – 0.107 Btu/lb-°F (21°C – 448 J/kg-°C) |
| Permeability ho 200 oersted |
|
| 76°F – 1.003 (24°C – 1.003) | |
| -109°F – 1.004 (-78°C – 1.004) | |
| -320°F - 1.016 (-196°C – 1.016) | |
| Mocheso oa Curie | <-320°F (<-196°C) |
Lisebelisoa
l Lisebelisoa tsa mocheso o phahameng indastering ea likoloi le sebaka sa lifofane-li-rotor tsa turbocharger le litiiso (tšebeliso e hlokomelehang ke Mazda RX-7 mofuta oa boraro), lienjineri tsa rotary (lithuthuthu tsa Norton), Foromo ea 1 le litsamaiso tsa ho tima tsa NASCAR;
l Lisebelisoa tsa mocheso o phahameng sebakeng sa sefofane-mahare a turbine ea khase le liringche tsa ho boloka, litiiso le li-combustors, litima-motei tsa enjene ea jete, lithapo tsa makotikoti a tukang, le li-diffuser tse kopanyang;
l Thepa ea ho futhumatsa mocheso-libaskete, literei le lisebelisoa tsa ho kenya, carburizing, carbonitriding, nitriding bakeng sa lits'ebetso tse futhumatsang indasteri, le ka har'a li-tubes tse khanyang, li-muffles, li-retorts, lithebe tsa malakabe, li-tubes tse koalang likhoele, mabanta a tsamaisang terata e lohiloeng, le lisebelisoa tse futhumatsang tsa motlakase indastering. libopi;
l Ho sebetsana le lik'hemik'hale-ho kenya makotikoti ho li-reformers tsa ammonia le lisebelisoa tsa tlhahiso ea nitric acid;
l Phekolo ea lik'hemik'hale-lijenereithara le li-preheaters tsa moea;
l Lits'ebetso tsa taolo ea tšilafalo-liphaposi tse tukang ka har'a licheso tsa litšila tse tiileng;
l Sebaka sa tlhahiso ea matla-superheater tube e tšehetsa litšitiso tsa grid le ho tšoara molora
Nako ea poso: Oct-14-2021