How to reduce the loss of seamless steel pipes
Date: 2021-11-16
How to reduce the loss of seamless steel pipes?
The application range of seamless steel pipes(astm a106 steel pipes) is becoming wider and wider. In the whole process of applying seamless steel pipes, how should people keep the level of seamless steel pipes unchanged?
Improve the gloss and overall wear resistance of the seamless steel pipe surface layer, thereby prolonging the service life. The key is that it can improve the integration with other conventional metal materials. At this stage, for the stainless steel passivation of seamless steel pipes, the key to using chromate for passivation is to increase some activation in the case of passivation. After passivation, reagents such as chloride, ammonium sulfate or hydrochloric acid will cause the chromate film to thicken. When the passivating agent contains chloride, it can reduce the interfacial tension of the steel chain, accelerate the demulsification reaction, improve the chemical polishing effect, and make the coating delicate and bright.
Seamless steel pipes must not only pay attention to the relevant production process when manufacturing, but also ensure the accuracy of the middle and late production processing and technical solutions, so as to add double protection to the finished product and the seamless steel pipe. The steel pipe not only needs to improve the quality in appearance, but also has become a raw material with strong processing ability at this stage.
Improve the arc accuracy of the casting machine to prevent excessive ground stress on the heterogeneous page at the initial stage of condensation and avoid cracks along the grain boundary.
Use the method of appropriately speeding up the forging seamless pipe and expanding the cooling water flow within a certain range, increasing the water flow and lowering the temperature to maintain forced cooling.
Strictly control the composition of steel grades, especially in terms of controlling carbon and water content.
The seamless tube improves the electromagnetic induction mixing of the rolled steel and controls the superheat of the molten steel in the tundish below 40°C.
Post time: Nov-16-2021